YUCERA Dental Materials And Equipment Manufacturer False Teeth Material Color Zirconia Blocks
Dental Zirconia Blocks Features
Zirconium dioxide porcelain tooth is a mineral that exists in nature as oblique zircon. Its density and strength are very high, the strength is 1.5 times higher than that of EMPRESS II, more than 60% higher than INCERAM zirconia, combined with unique crack resistance and strong curing performance after cracking, it can make porcelain bridges of more than 6 units. The problem that all all-ceramic systems cannot be used as long bridges is solved.
Dental Zirconia Blocks Advantages
Compared with other all-ceramic restoration materials, the strength of zirconia material allows doctors to achieve extremely high strength without too much abrasion of the patient’s real teeth. Among them, Vita all-ceramic plus yttrium stabilizes zirconia. It is also known as ceramic steel.
Our service
1, Yucera establish cooperation with many large denture processing center and oral hospitals, get outstanding performance in the field and earn good reputation amount technicians and patients.
2, We have already passed the CE and ISO certification.
I’m sure that our factory is good enough for your program in your market.
Welcome any comments.
HT/ST Sintering Curve (1-5)
| HT/ST Sintering Curve (1-5) |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 150 | 6 |
| Step 3 | 1200 | 1530 | 110 | 3 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 100 | -7.3 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
HT/ST Sintering Curve (10 units)
| HT/ST Sintering Curve (10 units) |
| Sintering step | Start Temperature(℃) | End Temperature(℃) | Time(Min) | Rate(℃/Min) |
| Step 1 | 20 | 300 | 30 | 9.3 |
| Step 2 | 300 | 1200 | 190 | 4.7 |
| Step 3 | 1200 | 1530 | 150 | 2.2 |
| Step 4 | 1530 | 1530 | 120 | 0 |
| Step 5 | 1530 | 800 | 120 | -6 |
| Step 6 | 800 | natural cooling 20 | 120 | -6.5 |
ST Color Dental Zirconia Blocks
* Pre-shaded technics
* Uniform color
* Without post dyeing posses
* Suitable for full contour crown, bridge and anterior
Indications
Crown, Inlay, Onlay, 2-5 unit Bridges, Anterior
Physical Characteristics
| Physical Characteristics |
| Sintered density 6.07±0.01g/cm³ |
| Bending Strength 1100 MPa |
| Transmittance 45% |
| Hardness 1200HV |
| Sintering temperature 1480~1550℃/recommend 1530℃ |